Abstract
This project was carried out with the objective of obtaining the strength properties of I-joist made from oriented strand board (OSB) web with L-butt joint and solid araucaria (araucaria hunsteinii) wood flanges. The result shows that sample 1 (A01) had the lowest value of MOR with 17.5 MPa and the lowest value of MOE was sample 2 (A02) with 9646 MPa. The highest value of MOE and MOR was by sample 3 (A03) with 13500 MPa and 24.8 MPa. The location of I-joist failure was at the web joint. Failures happen at the gap joint because of the glue were not spread evenly. Araucaria hunsteinii is a soft wood species and it was use to make part of l-joist flanges. This study proved that Araucaria hunsteinii can be used as flanges in I-joist system. This is because Araucaria hunsteinii and OSB can perform as a system of I-joist. This study try to promote Araucaria hunsteinii in building structure system.
Metadata
Item Type: | Student Project |
---|---|
Creators: | Creators Email / ID Num. Md Hassan, Muhammad Nadmin UNSPECIFIED |
Subjects: | T Technology > TS Manufactures > Wood technology. Lumber > Wood products. Furniture T Technology > TS Manufactures > Engineered wood. Fiberboard, particle board, etc. |
Divisions: | Universiti Teknologi MARA, Pahang > Jengka Campus > Faculty of Applied Sciences Universiti Teknologi MARA, Pahang > Jengka Campus |
Programme: | Diploma in Wood Industry |
Keywords: | I-joist, oriented strand board (OSB), araucaria hunsteinii |
Date: | 2001 |
URI: | https://ir.uitm.edu.my/id/eprint/107099 |
Download
![[thumbnail of 107099.PDF]](https://ir.uitm.edu.my/style/images/fileicons/text.png)
107099.PDF
Download (952kB)
Digital Copy

Physical Copy

ID Number
107099
Indexing


Statistic