Properties of particleboard using treated and untreated sugarcane bagasse / Muhammad Sideq Md Yunos

Md Yunos, Muhammad Sideq (2014) Properties of particleboard using treated and untreated sugarcane bagasse / Muhammad Sideq Md Yunos. [Student Project] (Unpublished)

Abstract

The main objective of this study is to investigate some of applied properties of experimental particleboards made with sugarcane bagasse, as an alternative fibrous raw material. Modulus of elasticity (MOE), modulus of rupture (MOR), internal bonding (IB), and thickness swelling (TS) of the sample were evaluate. Mats with target board density 700 kg/m3 were formed by using 7% resin content of phenol formaldehyde. Variable factor were a sugarcane bagasse particle size (l.0mm, 2.0mm, mix 1.0mm+2.0mm) and treated and untreated sugarcane bagasse. The treatment are made by soaking the sugarcane bagasse at warm water for 24 hours. From the result, particleboard made from treated sugarcane bagasse had the highest MOR and MOE result.

Metadata

Item Type: Student Project
Creators:
Creators
Email / ID Num.
Md Yunos, Muhammad Sideq
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Advisor
Abdullah, Zaimatul Aqmar
UNSPECIFIED
Subjects: S Agriculture > SB Plant culture > Sugar crops. Sugar plants > Sugarcane
T Technology > TS Manufactures > Engineered wood. Fiberboard, particle board, etc.
T Technology > TS Manufactures > Wood technology. Lumber > Chemical processing of wood
Divisions: Universiti Teknologi MARA, Pahang > Jengka Campus > Faculty of Applied Sciences
Programme: Bachelor of Science (Hons.) Furniture Technology
Keywords: Particleboard, sugarcane bagasse, bending strength
Date: 2014
URI: https://ir.uitm.edu.my/id/eprint/76708
Edit Item
Edit Item

Download

[thumbnail of 76708.PDF] Text
76708.PDF

Download (1MB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:
On Shelf

ID Number

76708

Indexing

Statistic

Statistic details