Abstract
The defects of the Lack of Fusion (LOF) and Lack of Penetration (LOP) on the surface of aluminium alloy 5083 and stainless steel 304L similar welding samples has been investigate using the advance Ultrasonic Testing (UT) Time of Flight Diffraction (TOFD) technique. The welding that was used to weld both similar samples is Tungsten Inert Gas (TIG) welding also known as Gas Tungsten Arc Welding (GTAW) and defects were made by the Die-sinking Electric Discharge Machine (EDM). There were total of three different types of Lack of Fusion (LOF) defects on both welded samples which are transverse surface, longitudinal surface and oblique, and another two Lack of Penetration (LOP) defects also on both welded samples. The defects were detected and investigated by Time of Flight Diffraction (TOFD) technique by observe the results of A-scan and B-scan images.
Metadata
Item Type: | Thesis (Degree) |
---|---|
Creators: | Creators Email / ID Num. Mohd Yasin, Mohamad Izad Asyaari UNSPECIFIED |
Contributors: | Contribution Name Email / ID Num. Thesis advisor Syed Yahya, Syed Yusainee (Dr) UNSPECIFIED |
Subjects: | T Technology > TS Manufactures > Production management. Operations management T Technology > TS Manufactures > Metal manufactures. Metalworking > Welding |
Divisions: | Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences |
Programme: | Bachelor of Science (Hons.) Physics |
Keywords: | Lack of Fusion, Lack of Penetration, Stainless steel 304L |
Date: | 2012 |
URI: | https://ir.uitm.edu.my/id/eprint/48515 |
Download
48515.pdf
Download (97kB)