Effects of filler concentration on the ionic conductivity of PVC+ (NH4)HS04 + A1203 (80nm) polymer electrolytes / Noor Shuhada Hamzah.
[Student Project]
(Unpublished)
Abstract
In this work nanocomposite polymer electrolytes based on PVC is the host polymer with (NKOHSCU as the doping salt in different ratios and have been preapared. AI2O3 (80nm), an inorganic filler were added to the highest conducting sample of PVC- (NH4)HS04 polymer electrolytes in order to enhance the conductivity to higher values. The highest conductivity was achieved for PVC-(NH4)HS04- AI2O3 (80nm) with concentration A1203 with 94 wt % of PVC -(NH4)HS04 and 6 wt % of A1203 with a value 3.75E-05 Son1 The rise in conductivity with additional of AI2O3 attributed to the filler helped to generate more charge carriers.
Metadata
Item Type: | Student Project |
---|---|
Creators: | Creators Email / ID Num. Hamzah, Shuhada UNSPECIFIED |
Contributors: | Contribution Name Email / ID Num. Thesis advisor Yahaya Subban, Ri Hanum (Prof. Dr.) UNSPECIFIED |
Subjects: | Q Science > QC Physics > Heat > Thermal conductivity Q Science > QC Physics > Electron |
Divisions: | Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences |
Programme: | Bachelor of Science (Hons.) Industrial Physics |
Keywords: | Ionic conductivity, Filler concentration, Polymer electrolytes |
Date: | 2011 |
URI: | https://ir.uitm.edu.my/id/eprint/45026 |
Download
Text
45026.pdf
Download (104kB)
45026.pdf
Download (104kB)
Digital Copy
Digital (fulltext) is available at:
Physical Copy
Physical status and holdings:
Item Status:
On Shelf