Properties of thermoplastic composite from anthocephalus chinensis: influence of filler content / Mohamad Sam Ropilah

Ropilah, Mohamad Sam (2003) Properties of thermoplastic composite from anthocephalus chinensis: influence of filler content / Mohamad Sam Ropilah. [Student Project] (Unpublished)

Abstract

The study carried out is to determine the properties of Kelempayan as thermoplastic composite. This study was carried out using the unscreened mesh and mesh with size of 60 and 80. The study was also use different percentage of filler content (10%, 15&, 20%). From the study, 15% of filler content shows the highest value for flexural MOR, followed by 20% mesh 80. The best result should be 20% mesh 80. The same result goes to FMOE with the value of 1528.89 Mpa. For TMOR the highest result is 10% mesh 80 and for TMOR the highest result is 60 mesh 20%. While for water absorption the lowest value is 60 mesh 15% with the value of 0.254%. From the study, thermoplastic composite from Kelempayan can be produce but depend on the purpose and the uses of the product.

Metadata

Item Type: Student Project
Creators:
Creators
Email / ID Num.
Ropilah, Mohamad Sam
UNSPECIFIED
Subjects: T Technology > TS Manufactures > Wood technology. Lumber > Wood products. Furniture
T Technology > TS Manufactures > Wood technology. Lumber > Chemical processing of wood
Divisions: Universiti Teknologi MARA, Pahang > Jengka Campus > Faculty of Applied Sciences
Universiti Teknologi MARA, Pahang > Jengka Campus
Programme: Diploma in Wood Industry
Keywords: Kelempayan, thermoplastic composite, anthoceplalus chinnensis
Date: 2003
URI: https://ir.uitm.edu.my/id/eprint/108695
Edit Item
Edit Item

Download

[thumbnail of 108695.PDF] Text
108695.PDF

Download (819kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:
On Shelf

ID Number

108695

Indexing

Statistic

Loading...

Statistic details