Metallographic observation: annealing and quenching on aluminum and mild steel / Batrisyia Rojitan

Rojitan, Batrisyia (2023) Metallographic observation: annealing and quenching on aluminum and mild steel / Batrisyia Rojitan. [Student Project] (Unpublished)

Abstract

The objectives of this project are to observe the hardness reaction by using Vickers hardness test towards high temperature reaction for a given time and to differentiate the microstructure features between aluminum and mild steel that undergoes annealing and quenching process. Annealing and Quenching process will be carried out vary on the specimens. For aluminum, annealing and quenching use 450 °C for 1 hour and 15 minutes respectively. Mild steel use 800 °C and 950 °C for 2 hours for annealing and quenching process respectively. Water quench is being used for both metal's quenching process. The result is obtaining the hardness value of aluminum and mild steel specimens. To conclude, the study is projected to relate the relationship of heat treatment process and hardness value of aluminum and mild steel.

Metadata

Item Type: Student Project
Creators:
Creators
Email / ID Num.
Rojitan, Batrisyia
2021625072
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Abdullah, Shukriah
UNSPECIFIED
Subjects: T Technology > TA Engineering. Civil engineering > Materials of engineering and construction > Physical properties > Surface effects and tests
Divisions: Universiti Teknologi MARA, Terengganu > Bukit Besi Campus > Faculty of Mechanical Engineering
Programme: Diploma in Mechanical Engineering
Keywords: Observe The Hardness Reaction, Vickers Hardness Test
Date: 2023
URI: https://ir.uitm.edu.my/id/eprint/105517
Edit Item
Edit Item

Download

[thumbnail of 105517.pdf] Text
105517.pdf
Download (69kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:

ID Number

105517

Indexing

Statistic

Statistic details