Characteristics of ionic conductivity in lithium salt onto MG30 polymer electrolyte / Nor Fazila Mahamad Yusoff

Mahamad Yusoff, Nor Fazila (2012) Characteristics of ionic conductivity in lithium salt onto MG30 polymer electrolyte / Nor Fazila Mahamad Yusoff. [Student Project] (Unpublished)

Abstract

A 30% PMMA-grafted natural rubber (MG30), lithium triflouromethanesulfonate (LiCF3S03 or LiTf ) and dimethyl carbonate (DMC) as a plasticizer were dissolved in tetrahydroforan (THF) as a solvent in the preparation of the solid polymer and gel polymers electrolytes (SPEs and GPEs). The ionic conductivity was characterized by using Impedance Spectroscopy (IS) at room temperature. The highest of conductivity value of SPE with composition of MG30 - 35 wt% UCF3SO3 is 39.05x10"5 S cm"1 at room temperature. SPE with highest conductivity was added with different weight percent of DMC plasticizer to form a GPE. The GPE with highest conductivity is 21.24xl0"5 S cm"1 at composition of 30 wt% of DMC plasticizer at room temperature. The polymer salt complexes were investigated using Fourier - Transform Infrared (FTIR) at room temperature within the frequency range of 4000-500 cm-1.

Metadata

Item Type: Student Project
Creators:
Creators
Email / ID Num.
Mahamad Yusoff, Nor Fazila
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Ali, Ab. Malik Marwan (Prof. Madya Dr.)
UNSPECIFIED
Subjects: Q Science > QC Physics > Heat > Thermal conductivity
Q Science > QC Physics > Electricity and magnetism
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Degree of Bachelor of Science (Hons.) Physic
Keywords: lithium salt, polymer, electrolyte
Date: July 2012
URI: https://ir.uitm.edu.my/id/eprint/43945
Edit Item
Edit Item

Download

[thumbnail of 43945.pdf] Text
43945.pdf

Download (106kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:
On Shelf

ID Number

43945

Indexing

Statistic

Statistic details