Electrochemical and mechanical properties of binder system mixed with nano-clay / Siti Mas Zalina Razali

Razali, Siti Mas Zalina (2008) Electrochemical and mechanical properties of binder system mixed with nano-clay / Siti Mas Zalina Razali. Degree thesis, Universiti Teknologi MARA (UiTM).

Abstract

The purposes of this thesis were to investigate the mechanical and electrochemical properties of coating system. A Dammar-Polyol binder system was examined by adding with nano-clay, Bentonite. The coating system was coated on Aluminium Q-panel as substrate. Curing time was taken five days before coating were tested by using cross-hatch test (ASTM D 3359-87) and impact test. The results were presented in term of damage grids in each sample and investigated the extent of the coating ability toward adhesion. Both of two tests showed a similar result in which the good performance was performed in 0.2 D sample which containing 20 wt% of dammar. Meanwhile, coating resistance, Rc, property of sample was characterized by electrochemical impedance spectroscopy, EIS, while the coated substrate was immersed in 3wt% of NaCl for 30 days. The result indicated that the 0.5 D which containing 50 wt% of dammar showed higher coating resistance than the other samples. However, the mixing of nano-clay into the Dammar-Polyol binder system was resulted the coating resistance of the sample became worse. But the addition of nano-clay was enhanced the mechanical properties of Dammar-polyol binder system.

Metadata

Item Type: Thesis (Degree)
Creators:
Creators
Email / ID Num.
Razali, Siti Mas Zalina
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Advisor
Ahmad, Azizah Hanom
UNSPECIFIED
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Bachelor Of Science (Hons.) Chemistry
Date: 2008
URI: https://ir.uitm.edu.my/id/eprint/99986
Edit Item
Edit Item

Download

[thumbnail of 99986.pdf] Text
99986.pdf

Download (136kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:

ID Number

99986

Indexing

Statistic

Statistic details