Preparation and characterization of plasticized ethylene carbonate (EC) on cellulose- NH4I electrolyte / Marini Musataffa.

Musataffa, Marini (2008) Preparation and characterization of plasticized ethylene carbonate (EC) on cellulose- NH4I electrolyte / Marini Musataffa. [Student Project] (Unpublished)

Abstract

In this study, cellulose acetate (CA) containing different concentration of ammonium iodide (NH4I) salt were prepared using a solution cast technique. The optimum percentage of salt and plasticizer that gave the highest value of electrical conductivity of the sample was determined. Impedance spectroscopy technique was carried out in order to determine the electrical conductivity value. The highest conductivity value was 3.7515xl0-5 Scm-1 for 1 g CA at 35 wt % ammonium iodide at 303 K. This conductivity was calculated using the bulk resistance value which can be obtained from the complex impedance plot in frequency range between 100 Hz and 1 MHz. The same procedure was repeated in order to prepare plasticized samples with ethylene carbonate (EC) using the optimum concentration of salted sample. The highest conductivity was 3.4396x10-4 Scm-1 at 40 wt % EC. Finally, the highest conducting plasticized sample was characterized using impedance spectroscopy at different temperatures from 303K to 373K.

Metadata

Item Type: Student Project
Creators:
Creators
Email / ID Num.
Musataffa, Marini
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Yahya, Muhd Zu Azhan (Dr.)
UNSPECIFIED
Subjects: Q Science > QD Chemistry > Physical and theoretical chemistry > Electrolytes, electrolyte solutions
T Technology > TP Chemical technology > Industrial radiochemistry. Industrial radiation chemistry
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Bachelor of Science (Hons.) Physics
Keywords: Plasticized ethylene carbonate, Cellulose acetate, Ammonium iodide
Date: 2008
URI: https://ir.uitm.edu.my/id/eprint/46749
Edit Item
Edit Item

Download

[thumbnail of 46749.pdf] Text
46749.pdf

Download (133kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:
On Shelf

ID Number

46749

Indexing

Statistic

Statistic details