Preparation and characterization by impedance spectroscopy of Si0₂ filled PVC-based polymer electrolyte system / Nor Hazlizaaini Basri

Basri, Nor Hazlizaaini (2007) Preparation and characterization by impedance spectroscopy of Si0₂ filled PVC-based polymer electrolyte system / Nor Hazlizaaini Basri. [Student Project] (Unpublished)

Abstract

Nano-composite polymer electrolyte with PVC as host polymer, Lithium triflate, LiCF3S03 as doping salt and silicon dioxide, Si02 as filler was studied. Impedance Spectroscopy was used to determine the ionic conductivity at room temperature. The ionic conductivity of pure PVC was 1.04 x 10"10 Scm"1. The addition of LiCF3S03 significantly improved the ionic conductivity of PVC. The film with 40 wt% of LiCF3S03 showed the highest ionic conductivity of 1.017 x 10"7 Scm"1. The polymer salt composition with the highest conductivity was added with filler, SiC>2 with a various percentage of weight. The ionic conductivity of PVC + LiCF3S03 + SiC>2 increased from 10'7 to 10"5 Scm'1. PVC + LiCF3S03 films with 8 wt% of Si02 showed the highest ionic conductivity value of 1.070 x 10"5 Scm"1.

Metadata

Item Type: Student Project
Creators:
Creators
Email / ID Num.
Basri, Nor Hazlizaaini
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Mohd Nor, Asiah
UNSPECIFIED
Subjects: Q Science > QD Chemistry > Physical and theoretical chemistry > Electrolytes, electrolyte solutions
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Degree of Bachelor of Science (Hons.) Physic
Keywords: spectroscopy, polymer, electrolyte
Date: May 2007
URI: https://ir.uitm.edu.my/id/eprint/46421
Edit Item
Edit Item

Download

[thumbnail of 46421.pdf] Text
46421.pdf

Download (119kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:
On Shelf

ID Number

46421

Indexing

Statistic

Statistic details