Comparisons between XRD of different ball-milled samples of LiNij.xCoxFey02 and LiNii.xCoxAly02 / Nurdalila Mohd Nazeri

Mohd Nazeri, Nurdalila (2012) Comparisons between XRD of different ball-milled samples of LiNij.xCoxFey02 and LiNii.xCoxAly02 / Nurdalila Mohd Nazeri. [Student Project] (Unpublished)
Abstract

LiNio.7Goo.2Feo.1O2 and LiNio.7Coo.2Alo.1O2 with micron sized particle was prepared to obtain nano sized particle by using high energy ball milling (HEBM) method. After the milling process, it causes in reducing the crystallite sizes and more agglomerations to the samples. X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) were used to characterize the samples and all the results were analysed and discussed. The 24 hours of milling has changed the samples from micron size to nano size by using 0.3mm and 0.5mm diameter balls.

Item Details
Item Type: Student Project
Creators:
Creators
Email / ID Num.
Mohd Nazeri, Nurdalila
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Kamarulzaman, Norlida (Prof. Dr.)
UNSPECIFIED
Subjects: Q Science > QC Physics > Descriptive and experimental mechanics
Q Science > QC Physics > Mathematical physics
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Bachelor of Science (Hons.) Industrial Physics
Keywords: High energ, Ball milling (HEBM), Particle, Micron
Date: 2012
URI: https://ir.uitm.edu.my/id/eprint/45392
Edit Item
Edit Item
Downloads & Files
[thumbnail of 45392.pdf]
Text
45392.pdf
Download (90kB)
Location & Physical Holdings
Digital Copy
Physical Location
  • Koleksi Akses Terhad | PTAR Utama | Shah Alam
Item Status
On Shelf
Indexing & Metrics
Google Scholar BASE