Shear Strength of the Mixed Adhesive Joint Silyl Modified Polymer-Epoxy in Single Lap Joint Aluminum Triyono / Sri Hastuti and Neng Sri Suharty

Triyono, Sri Hastuti and Neng, Sri Suharty (2017) Shear Strength of the Mixed Adhesive Joint Silyl Modified Polymer-Epoxy in Single Lap Joint Aluminum Triyono / Sri Hastuti and Neng Sri Suharty. Journal of Mechanical Engineering (JMechE), SI 4 (1). pp. 235-248. ISSN 18235514

Abstract

Shear strength of mixed adhesive joints (MAJ) silyl modified polymer (SMP)–epoxy (EP) in a single lap joint (SLJ) aluminum to aluminum has been investigated. Single lap joint specimens were made according to ASTM D-1002 standard. Three levels of mixed adhesive thickness of 0.2; 0.4; and 0.6 mm were used while the variations of mixed adhesive composition were 100%EP, 75%SMP:25%EP, 50%SMP:50%EP, 25%SMP:75%EP, 100%SMP. Sandpapering grid of 150 and acetone cleaning was performed on Aluminum surface. The pressure of 0.1 Mpa and post-curing of 100oC for 100 minutes were subjected on the mixed adhesive joint specimens. Shear tests and failure surface investigations were conducted to analyze the strength of the mixed adhesive joints. The addition of silyl modified polymer to epoxy decreases the shear strength and the shear modulus but increases the elongation of the mixed adhesive joints. The mixed-adhesive joint of 25%SMP:75%EP has the highest shear strength, even it is higher than that of the adhesive joint of 100%EP. There is no significant effect of ad

Metadata

Item Type: Article
Creators:
CreatorsEmail / ID. Num
Triyono, Sri Hastutitriyonomesin@uns.ac.id
Neng, Sri SuhartyUNSPECIFIED
Subjects: T Technology > TA Engineering. Civil engineering > Structural engineering
T Technology > TJ Mechanical engineering and machinery
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Mechanical Engineering
Journal or Publication Title: Journal of Mechanical Engineering (JMechE)
Journal: UiTM Journal > Journal of Mechanical Engineering (JMechE)
ISSN: 18235514
Volume: SI 4
Number: 1
Page Range: pp. 235-248
Item ID: 39265
Uncontrolled Keywords: Mixed Adhesive Joint, Silyl-Modified Polymer, Epoxy, Adhesive Thickness, Aluminum
URI: http://ir.uitm.edu.my/id/eprint/39265

Download

[img] Text
39265.pdf

Download (974kB)

Others


View in Google Scholar

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year