Abstract
Glass samples with the composition of xSrO-10PbO-(90-x)B2O3 (x = 20- 45), xPbO-30SrO-(70-x)B2O3 (x = 0-25) and xSrO-(90-x)B2O3-2CeO2- 8A1203 (x = 25-50 mol%) were prepared by melt-quenching method to elucidate the structural, elastic and optical behavior in borate anomaly region. Characterization techniques like X-ray diffraction (XRD), Fourier transforms infra-red spectroscopy (FTIR), ultrasonic measurement, UV-Visible and Luminescence (for SrO-B203-Ce02-A1203) spectroscopes are employed in the present work. XRD data showed amorphous nature for SrO-PbO-B203 samples while mixed crystalline/amorphous phases for the SrO-B203-Ce02-A1203 samples at x > 35 mol%. FESEM image and EDX analysis revealed that the samples contained Ce-rich crystalline phase and Ce depleted glass phase. FTIR analysis revealed the presence of B04 and B03 vibration groups. Variation of SrO in SrO-PbOB203 and SrO-B203-Ce02-A1203 samples has resulted in increased ultrasonic velocities, elastic moduli (CL, μ, K and Y), hardness (H), Debye temperature (9D) at lower SrO content but decreased for higher SrO addition…
Metadata
Item Type: | Book Section |
---|---|
Creators: | Creators Email / ID Num. Sabri, Nurul Syahidah UNSPECIFIED |
Subjects: | Q Science > QD Chemistry Q Science > QD Chemistry > Crystallography |
Divisions: | Universiti Teknologi MARA, Shah Alam > Institut Pengajian Siswazah (IPSis) : Institute of Graduate Studies (IGS) |
Series Name: | IGS Biannual Publication |
Volume: | 14 |
Keywords: | Abstract; Abstract of thesis; Newsletter; Research information; Doctoral graduates; IPSis; IGS; UiTM; Elastic |
Date: | 2018 |
URI: | https://ir.uitm.edu.my/id/eprint/22091 |
Download
ABS_NURUL SYAHIDAH SABRI TDRA VOL 14 IGS 18.pdf - Submitted Version
Download (5MB) | Preview