Properties of particle board from Bagasse (saccharum offlclnarum l) mix with unknown species of wood waste in relation to wood ratio and resin / Norsyazana Jasni

Jasni, Norsyazana (2017) Properties of particle board from Bagasse (saccharum offlclnarum l) mix with unknown species of wood waste in relation to wood ratio and resin / Norsyazana Jasni. [Student Project] (Unpublished)

Abstract

Properties of particleboard from bagasse (Saccharum officinarum L) mix with
unknown species of wood in relation to wood ratio and resin content bounded
with phenol formaldehyde has been studied. The particle board manufacturing
were made with four ratio 100 bagasse and 60: 40 by mix with different resin
content 9% and 11%. The boards produced were evaluated for its bending test
(BS), internal bond (IB), water absorption (WA) and thickness swelling (TS)
according to European Standard. The measurement of bending test used in this
study is 350mm X 50mm X 12mmand for IB, WA, TS 50mm X 50mm. By using
ratio 60 bagasse and 40 wood waste the board strength is good. The higher
percentage of resin content will produce the better of particleboard properties.
This study finds Bagasse can be the alternative new raw material in
manufacturing of composite panel product because it can replace the wood in
producing particle boards.

Metadata

Item Type:	Student Project
Creators:	Creators Email / ID Num. Jasni, Norsyazana UNSPECIFIED
Subjects:	H Social Sciences > HD Industries. Land use. Labor > Manufacturing industries > Furniture industry and trade T Technology > TP Chemical technology > Chemical engineering
Divisions:	Universiti Teknologi MARA, Pahang > Jengka Campus > Faculty of Applied Sciences
Keywords:	Properties of particleboard, Saccharum officinarum L, Wood ratio, Resin content, Phenol formaldehyde, Bagasse
Date:	2017
URI:	https://ir.uitm.edu.my/id/eprint/22750