Particle board from wood waste with size particle (1.0 mm) in relation to different board density and resin content / Mohd Shuaib Azali Zulkepli

Zulkepli, Mohd Shuaib Azali (2016) Particle board from wood waste with size particle (1.0 mm) in relation to different board density and resin content / Mohd Shuaib Azali Zulkepli. Student Project. Faculty of Applied Sciences, Jengka, Pahang. (Unpublished)

Abstract

Logging activity can cause low soil and habitat protection expires wood annually increased demand has decreased. In addition, this material is quite popular nowadays have adopted one of the external and internal wood furniture alternatives particleboard. In these studies, the main purpose, to determine the mechanical and physical properties, from wood waste has been used for different densities of particle board and the circuit board and the resin content of the raw material used in manufacturing. Two different circuit board density are using; 650 kg 1m3 Iow-density board and 750 kg/m3 high density board. 8%, 10% and 12% resin content was used as another parameter using urea formaldehyde as a binder. The results showed that 12% of particleboard with a resin content of less than 750 kg/m3 density board bending strength and internal bonding and thickness swelling and water absorption, the lowest value to a higher value.

Download

[img] Text
PPb_MOHD SHUAIB AZALI ZULKEPLI AS C 16_5.PDF

Download (1MB)

Metadata

Item Type: Monograph (Student Project)
Creators:
CreatorsID Num.
Zulkepli, Mohd Shuaib AzaliUNSPECIFIED
Subjects: T Technology > TS Manufactures > Production management. Operations management
T Technology > TS Manufactures > Wood technology. Lumber
Divisions: Universiti Teknologi MARA, Pahang > Jengka Campus > Faculty of Applied Sciences (C)
Item ID: 22681
Uncontrolled Keywords: Particleboard, Urea formaldehyde, Density board bending strength, Internal bonding
URI: http://ir.uitm.edu.my/id/eprint/22681

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year