A study on the effect of mechanical properties and rheologycal behaviour of polyproplene reinforced montmorillonite / Normuhaizah Mohd Zain

Mohd Zain, Normuhaizah (2010) A study on the effect of mechanical properties and rheologycal behaviour of polyproplene reinforced montmorillonite / Normuhaizah Mohd Zain. Degree thesis, Universiti Teknologi MARA.

Abstract

This research focused on the mechanical properties of polypropylene (PP) reinforced montmorillonite (MMT). The aim of this research is to determine the mechanical properties of PP/MMT nanocomposite with different concentration (2 wt%, 4 wt%, 6 wt% , 8 wt% and 10 wt%) of MMT. PP and MMT were mix by using Dispersion Mixer. The material was mixed at temperature 190°C. After that, the material was fabricated by using hot press with 190°C for both upper and lower compressor. Mechanical properties of the sample were evaluated by tensile test, impact test, and three-point bending test according to BS EN ISO 527, BS EN 60811 and BS 6319 respectively. From the tensile test, the result obtained shown that the sample of 2wt.% and for impact test shown 6wt.% of clay loading which has the better mechanical properties. The rheological behavior also determined. All the concentration have pseudoplastic, but the better pseudoplastic is 8wt.% of loading clay.

Metadata

Item Type: Thesis (Degree)
Creators:
Creators
Email / ID Num.
Mohd Zain, Normuhaizah
2006131637
Contributors:
Contribution
Name
Email / ID Num.
UNSPECIFIED
Wahab, Nor Aini (Prof.)
UNSPECIFIED
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Mechanical Engineering
Programme: Bachelor Engineering (Hons) (Mechanical)
Keywords: Mechanical properties, Rheologycal, Polyproplene
Date: May 2010
URI: https://ir.uitm.edu.my/id/eprint/64049
Edit Item
Edit Item

Download

[thumbnail of 64049.pdf] Text
64049.pdf

Download (97kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:
On Shelf

ID Number

64049

Indexing

Statistic

Statistic details