The effects of SQDNs properties coated by potassium / Noor Aida Roslan

Roslan, Noor Aida (2011) The effects of SQDNs properties coated by potassium / Noor Aida Roslan. [Student Project] (Unpublished)

Download

[thumbnail of 44241.pdf] Text
44241.pdf

Download (113kB)

Abstract

Silicon Quantum Dots nano particles (SQDNs) were formed by grinding the free standing of Porous silicon that have been formed by anodically etching p-type Si [100] wafer in hydrofluoric (HF) solution at 1:1 ratio of ethanol with increase current density to 50 mA/cm2. The samples were prepared by coating to different concentration of potassium which is 0.6 M, 0.8 M and 1.0 M. The samples were characterized by using SEM, UVVis, FTIR spectrometer and PL spectrometer. The Potassium was successful coated into SQDNs. The samples were immersed in 30 ml distilled water to investigate the Potassium absorption in SQDNs wash for four batches. The UV-Vis result show that more quantity of K release from SQDNs for 1st wash batch for all concentration. The FTIR spectrum show the amount of KNO3 released after wash for four batches. The coating SQDNs with KNO3 show the wavelengths shifted to longer on the PL intensity.

Metadata

Item Type: Student Project
Creators:
Creators
Email
Roslan, Noor Aida
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
UNSPECIFIED
UNSPECIFIED
Subjects: Q Science > QD Chemistry > Organic chemistry
Q Science > QD Chemistry > Analytical chemistry
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Degree of Bachelor of Science (Hons.) Physic
Item ID: 44241
Uncontrolled Keywords: potassium, SQDNs, silicon
URI: https://ir.uitm.edu.my/id/eprint/44241

Fulltext

Fulltext is available at:
  • Koleksi Akses Terhad | PTAR Utama | Shah Alam
  • ID Number

    44241

    Indexing


    View in Google Scholar

    Edit Item
    Edit Item