Mechanical and conductive properties of silicone filled graphene treated with silane coupling agent electrically conduvtive adhesive [ECAs] / Rabi’atul 'Adawiyah Mohd Yatim

Mohd Yatim, Rabi’atul 'Adawiyah (2020) Mechanical and conductive properties of silicone filled graphene treated with silane coupling agent electrically conduvtive adhesive [ECAs] / Rabi’atul 'Adawiyah Mohd Yatim. Degree thesis, Universiti Teknologi Mara Perlis.

Download

[thumbnail of 34594.pdf] Text
34594.pdf

Download (186kB)

Abstract

Graphene treated with silane-based silicone was successfully prepared for electrically conductive adhesive application via mechanical stirring process. The objectives of this study were to investigate the mechanical and conductive properties of various graphene loading (0, 1, 3, 5 wt%) filled silicone and determine the effect of silane treatment on graphene reinforcement in silicone electrically conductive adhesive different graphene/silane loading (0, 1, 3, and 5 wt%). Mechanical properties testing has been conducted via hardness test and tensile test whilst conductive properties testing using electrochemical impendence spectroscopy (EIS) and volume resistivity. For hardness testing, GR/APTES regardless of its loading have the higher value of hardness at 60. While as for tensile test, GR/silicone and silicone/GR/APTES show the increment of tensile strength value. Hence, it shows that properties of graphene itself are higher in strength since it does not affect when the pull-out test was carried out. 5% GR/APTES show the high value of tensile stress at 4.05 MPa compared to the untreated GR at 3.5 MPa. The increasing of the GR/APTES shown an improvement to the mechanical properties, due to the surface treatments of APTES itself giving better interaction. Other than that, electrical conductivity increased was found at 1.90E-08 S/cm at 5% GR/APTES, when the percentage of graphene loading increased. This inverse trend is recorded with volume resistivity. The volume resistivity decreased when the GR loading increased, such as 5% GR/APTES was found at 1.10E-3 Ohm.cm-1. Overall, the incorporation of graphene/silane into adhesive improve the mechanical and conductive properties and the optimum value was found at 5 % GR/APTES.

Metadata

Item Type: Thesis (Degree)
Creators:
Creators
Email
Mohd Yatim, Rabi’atul 'Adawiyah
216351591
Subjects: Q Science > QD Chemistry > Inorganic chemistry > Carbon disulfide. Graphene. Carbon
Q Science > QD Chemistry > Physical and theoretical chemistry
Q Science > QD Chemistry > Physical and theoretical chemistry > Electrochemistry. Electrolysis
Divisions: Universiti Teknologi MARA, Perlis > Arau Campus > Faculty of Applied Sciences
Programme: Bachelor of Science (Hons) Polymer Technology
Item ID: 34594
Uncontrolled Keywords: Mechanical ; Conductive Properties ; Silicone Filled Graphene Treated ; Silane Coupling Agent Electrically Conduvtive Adhesive (ECAs)
URI: https://ir.uitm.edu.my/id/eprint/34594

Fulltext

Fulltext is available at:
  • Bilik Koleksi Akses Terhad | Kampus Arau, Perlis
  • ID Number

    34594

    Indexing


    View in Google Scholar

    Edit Item
    Edit Item