Development and characterization of modified silicone – dammar coating resin / Rosnah Zakaria

Zakaria, Rosnah (2014) Development and characterization of modified silicone – dammar coating resin / Rosnah Zakaria. In: The Doctoral Research Abstracts. IPSis Biannual Publication, 5 (5). Institute of Graduate Studies, UiTM, Shah Alam.

Abstract

The purpose of this study is to develop and characterized the new modified silicone binder resin. The silicone, synthetic resin bought from Dow Corning Corp. and dammar bought from local supplier. Ten (10) samples were prepared and one of them was silicone resin without dammar. The samples were designated as SD0, SD5, SD10, SD15, SD20, SD25, SD30, SD35, SD40 and SD45. The mixture was coat onto aluminum q-panel using spin coater and left in room temperature for around 7 – 8 days for curing process. The cured samples were undergone the mechanical and electrochemical characteristic. The mechanical characterizations include viscosity, cross-hatch test, pull off test, wetting and impact test. Results for cross hatch test showed that 5-15 wt% of dammar in the silicone resin provide the better adhesion on aluminum q-panel with the edges of the cut are smooth and none of the square lattice detached. In the impact test, no fracture can be observed on the impact surfaces when the 1 kg load was released on SD0 – SD20 dried coating surfaces.

Metadata

Item Type: Book Section
Creators:
Creators
Email / ID Num.
Zakaria, Rosnah
UNSPECIFIED
Subjects: L Education > LB Theory and practice of education > Higher Education > Dissertations, Academic. Preparation of theses > Malaysia
Divisions: Universiti Teknologi MARA, Shah Alam > Institut Pengajian Siswazah (IPSis) : Institute of Graduate Studies (IGS)
Series Name: IPSis Biannual Publication
Volume: 5
Number: 5
Keywords: Abstract; Abstract of thesis; Newsletter; Research information; Doctoral graduates; IPSis; IGS; UiTM; dammar coating resin
Date: 2014
URI: https://ir.uitm.edu.my/id/eprint/19214
Edit Item
Edit Item

Download

[thumbnail of ABS_ROSNAH ZAKARIA TDRA VOL 5 IGS_14.pdf]
Preview
Text
ABS_ROSNAH ZAKARIA TDRA VOL 5 IGS_14.pdf

Download (461kB) | Preview

ID Number

19214

Indexing

Statistic

Statistic details