Effect of annealing temperature on the surface morphology of titanium dioxide thin films prepared by sol-gel method / Nur Khairani Samin

Samin, Nur Khairani (2008) Effect of annealing temperature on the surface morphology of titanium dioxide thin films prepared by sol-gel method / Nur Khairani Samin. [Student Project] (Unpublished)

Download

[thumbnail of 48749.pdf] Text
48749.pdf

Download (128kB)

Abstract

Titanium dioxide (Ti02) thin films have been prepared using sol gel method and deposited by spin coating technique. Ti02 thin films were deposited on silicon and glass substrates. The influence of annealing temperature from 300°C to 500°C on the surface morphology, structural and optical properties were characterized by Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD) and Ultraviolet visible spectroscopy (UV-Vis). The SEM image of thin film deposited on silicon substrate shows the grain boundary of Tid is large and decrease with higher annealing temperature. While for thin films deposited on glass substrate do not shows any significant difference as the annealing temperature increased. This might happen due to lattice mismatching. Structural properties from the XRD analysis show that the Ti02 thin film is nanocrystalline anatase phase. While UV-Vis shows the thin films has high transmittance percentage of visible light and fully absorb the UV light at wavelength of 300 nm.

Metadata

Item Type: Student Project
Creators:
Creators
Email
Samin, Nur Khairani
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Mohd Nor, Asiah
UNSPECIFIED
Subjects: Q Science > QC Physics > Heat
Q Science > QC Physics > Heat > Temperature measurements
Q Science > QC Physics > Heat > Temperature
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Bachelor of Science (Hons.) Physics
Item ID: 48749
Uncontrolled Keywords: Titanium dioxide (Ti02), Sol gel method, Coating technique
URI: https://ir.uitm.edu.my/id/eprint/48749

Fulltext

Fulltext is available at:
  • Koleksi Akses Terhad | PTAR Utama | Shah Alam
  • ID Number

    48749

    Indexing


    View in Google Scholar

    Edit Item
    Edit Item