Effect of Ca substitution on high temperature resistivity of Eu₁₋ₓCaₓBa₂Cu₃O₇₋ᴕ ceramics(x=0.0,0.1,0.5) / Mohamad Shahrizal Mohamad Salleh

Mohamad Salleh, Mohamad Shahrizal (2010) Effect of Ca substitution on high temperature resistivity of Eu₁₋ₓCaₓBa₂Cu₃O₇₋ᴕ ceramics(x=0.0,0.1,0.5) / Mohamad Shahrizal Mohamad Salleh. [Student Project] (Unpublished)

Download

[thumbnail of 44238.pdf] Text
44238.pdf

Download (111kB)

Abstract

In this paper, Eui-xCaxBa2CU307-a Ceramic rod with cross sections of 0.65mm x 0.65mm and length 12mm with x=0.0,x=0.1 and x=0.5 were prepared by standard solid state reaction. The rod shows various functional characteristics that give rise to applications in devices such as oxygen sensor. The temperature dependent test were measured by using four point probe method. The data is taken due to increasing of temperature. This sensor operates without any separate heater by taking advantage of the high temperature where oxide ions can diffuse easily. The values of voltage and current were obtained from the temperature dependent experiment. The resistivity value was calculated by using the equation. The result was expressed in a graph, it shows varies data for each sample. With the substitution of Ca in Eu site, the sensor is said to be more sensitive due to increasing of conductivity because of increasing in hole concentration.

Metadata

Item Type: Student Project
Creators:
Creators
Email
Mohamad Salleh, Mohamad Shahrizal
2007288854
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Hassan, Misbah
UNSPECIFIED
Subjects: Q Science > QC Physics > Descriptive and experimental mechanics
Q Science > QC Physics > Heat
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Degree of Bachelor of Science (Hons.) Physic
Item ID: 44238
Uncontrolled Keywords: ceramics, temperaure, rod
URI: https://ir.uitm.edu.my/id/eprint/44238

Fulltext

Fulltext is available at:
  • Koleksi Akses Terhad | PTAR Utama | Shah Alam
  • ID Number

    44238

    Indexing


    View in Google Scholar

    Edit Item
    Edit Item