Oxygen sensitive hot spot on ErBa₂Cu₃0₇₋δ ceramics / Mohd Narizee Mohd Nasir

Mohd Nasir, Mohd Narizee (2006) Oxygen sensitive hot spot on ErBa₂Cu₃0₇₋δ ceramics / Mohd Narizee Mohd Nasir. [Student Project] (Unpublished)

Download

[thumbnail of 44231.pdf] Text
44231.pdf

Download (110kB)

Abstract

In this paper, ErBa2Cu307-s composite ceramic rods with cross sections of 0.65mw x 0.65/?!??/ and various BaA^C^ contents were prepared by solid state reaction. A glowing hot spot appeared on the rods when a certain dc voltage was applied at ambient temperature in air and moves to the negative electrodes with the velocity of a few mm per minute. The hot spot appears by self heating of the local part on the ErBa2Cu3C?7.d ceramic rods. The rod with the hot spot shows various functional characteristics that give rise to applications in devices such as an oxygen sensor. The current - voltage characteristics were measured by using a four-point probe method. This sensor operates without any separate heater by taking advantage of the high temperature of the hot spot where oxide ions can diffuse easily. The oxygen concentration is determined from the value of the current flowing through the rods by utilizing the change in resistivity of the hot spot depending on oxygen partial pressure in atmosphere; For the evaluation of the sensing characteristics, the oxygen concentration was changed by using the mixture of oxygen and nitrogen. Oxygen concentrations of 0 to 100% can be detected with high sensitivity and the response time varies with different BaA^CU contents. With the addition of BaAhO^ the sensitivity performance of the rods decreases and its response time would increase. The proposed sensor using the hot spot not only has the great advantage of the simple structure but also the response performance of this sensor is almost the same as that of the limiting-current-type oxygen sensor using Zr02, operating at 500°C.

Metadata

Item Type: Student Project
Creators:
Creators
Email
Mohd Nasir, Mohd Narizee
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Yahya, Ahmad Kamal Hayati (Prof Dr )
UNSPECIFIED
Subjects: Q Science > QC Physics > Descriptive and experimental mechanics
Q Science > QC Physics > Heat
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Degree of Bachelor of Science (Hons.) Physic
Item ID: 44231
Uncontrolled Keywords: ceramics, oxygen, electrodes
URI: https://ir.uitm.edu.my/id/eprint/44231

Fulltext

Fulltext is available at:
  • Koleksi Akses Terhad | PTAR Utama | Shah Alam
  • ID Number

    44231

    Indexing


    View in Google Scholar

    Edit Item
    Edit Item