Zainal Abidin, Zuliana Salmee (2012) Properties of ca doped in non-porous and porous of Y3CaBa4Cu8Oy compared to non-porous and porous of YBa2Cu3Oy ceramics / Zuliana Salmee Zainal Abidin. [Student Project] (Unpublished)

Abstract

All samples powder were prepared using solid state method involved a series of heating and grinding. Ca was doped in Ba site of Y3Ba4CusOy superconductor. Sucrose was adding during pelletization and after that firing at 400°C in a furnace, open pores were created. Then all samples were final sintered at 950°C in open atmosphere. These samples characterized through using the X^ay diffraction (XRD) for phase evaluation, scanning electron microscopy (SEM) for grain morphology, and He closed cycle four point probe to determine the critical temperature, Tc and critical current density, Jc, Experimental results showed that the critical temperature, Tc depends on Ca substitution. When Ca doped in YaBa^ugOy, the value of critical temperature decreased, it is lower than critical temperature of YBa2Cu30y. From the graph represent resistivity versus temperature, the major phase is orthorhombic and most of the sample shows metallic behaviour.

Metadata

Item Type: Student Project
Creators:
Creators
Email / ID Num.
Zainal Abidin, Zuliana Salmee
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Hashim, Azhan (Dr.)
UNSPECIFIED
Subjects: Q Science > QC Physics > Descriptive and experimental mechanics
Q Science > QC Physics > Mathematical physics
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Degree of Bachelor of Science (Hons.) Physic
Keywords: powder, porous, heating
Date: January 2012
URI: https://ir.uitm.edu.my/id/eprint/44012
Edit Item
Edit Item

Download

[thumbnail of 44012.pdf] Text
44012.pdf

Download (112kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:

ID Number

44012

Indexing

Statistic

Statistic details