Effect of hydrogen peroxide (H202) in porous silicon as nitrogen gas sensor / Tahirah Mat Waijar

Mat Waijar, Tahirah (2012) Effect of hydrogen peroxide (H202) in porous silicon as nitrogen gas sensor / Tahirah Mat Waijar. [Student Project] (Unpublished)

Download

[thumbnail of 44008.pdf] Text
44008.pdf

Download (122kB)

Abstract

The effects of Hydrogen Peroxide (H202) in porous silicon to detect Nitrogen gas were investigated. Three major types and another extra two types of PSi samples have been prepared. One of the PSi sample prepared with typical HF anodizing solution and other two major samples anodized with the presence of H202 in 20 minutes (30% and 35% respectively) in the solution. Then, another two samples were prepared with presence of 35% concentration of H202 in 10 minutes and 30 minutes respectively. Samples anodized with H202 solution showed a porous silicon structure with higher porosity compared to those not treated with H202 that shown through micrograph of FESEM. Then, samples that anodized with presence of 35% concentration of H202 in 30 minutes etching time show more porous than sample that used similar solution for 10 minutes etching time. Moreover, effect of H202 based porous silicon sample fabricated as nitrogen gas sensor showed better electrical (I-V) sensitivity compared to those without H202.

Metadata

Item Type: Student Project
Creators:
Creators
Email
Mat Waijar, Tahirah
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Abdullah, Saifollah (Prof. Dr. )
UNSPECIFIED
Subjects: Q Science > QC Physics > Electricity and magnetism
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Degree of Bachelor of Science (Hons.) Physic
Item ID: 44008
Uncontrolled Keywords: hydrogen peroxide, nitrogen, silicon
URI: https://ir.uitm.edu.my/id/eprint/44008

Fulltext

Fulltext is available at:
  • Koleksi Akses Terhad | PTAR Utama | Shah Alam
  • ID Number

    44008

    Indexing


    View in Google Scholar

    Edit Item
    Edit Item