From rice husk to transparent radiation protection material / Iskandar Shahrim Mustafa... [et al.]

Mustafa, Iskandar Shahrim and Razali, Nur Ain Nabilah and Ibrahim, Abdul Razak and Yahaya, Nor Zakiah and Kamari, Halimah Mohamed (2016) From rice husk to transparent radiation protection material / Iskandar Shahrim Mustafa... [et al.]. Jurnal Intelek, 9 (2). pp. 1-6. ISSN 2682-9223

Download

[thumbnail of 35294.pdf] Text
35294.pdf

Download (420kB)

Abstract

High amount of silica (SiO2) content, 99.36% was successfully prepared from Rice Husk Ash (RHA) through the burning of rice husk. Eventually, quaternary glasses were fabricated using melt quenching technique based on chemical compound composition xBi2O3 - (1-x)ZnO - 0.2B2O3 - 0.3(SiO2)RHA. The final thickness of glass samples prepared was within ~3.41mm. As the mole percentages of Bi2O3 increased, the glass density and molar volume was also increased from 4.45 gcm-1 to 6.60 gcm-1. The increment is due to larger atomic number of Bi3+ compared to the Si2+, B3+ and Zn in the glass samples. However, the oxygen packing density decreased as mole percentages of Bi2O3 were increased from 240.44 g-atom/l to 161.24 g-atom/l. The decreasing in oxygen packing density was due to the high non-bridging oxygen in the glass samples. The radiation attenuation parameterization was measured using 241Am as source of gamma ray interactions at energy 59.54 keV. The mass attenuation coefficient increased from 0.53cm2g-1 to 5.12cm2g-1 relatively towards the increment of Bi2O3 mole percentages. The phenomenon is due to the escalating in photoelectric absorption effect and declining in the Compton scattering caused by high atomic number of Bi3+ in the glass samples. Using Lorentz-Lorentz formulation, the refractive index obtained for glass samples prepared was within favourable range from 1.97 to 1.73.

Metadata

Item Type: Article
Creators:
Creators
Email
Mustafa, Iskandar Shahrim
UNSPECIFIED
Razali, Nur Ain Nabilah
UNSPECIFIED
Ibrahim, Abdul Razak
UNSPECIFIED
Yahaya, Nor Zakiah
UNSPECIFIED
Kamari, Halimah Mohamed
UNSPECIFIED
Subjects: Q Science > QD Chemistry > Organic chemistry > Polymers. Macromolecules
T Technology > TP Chemical technology > Clay industries. Ceramics. Glass
Divisions: Universiti Teknologi MARA, Perlis > Arau Campus
Journal or Publication Title: Jurnal Intelek
UiTM Journal Collections: UiTM Journal > Jurnal Intelek (JI)
ISSN: 2682-9223
Volume: 9
Number: 2
Page Range: pp. 1-6
Official URL: https://jurnalintelek.uitm.edu.my/index.php/main
Item ID: 35294
Uncontrolled Keywords: Rice husk, Glass, Radiation, Attenuation
URI: https://ir.uitm.edu.my/id/eprint/35294

ID Number

35294

Indexing


View in Google Scholar

Edit Item
Edit Item