Strength and behavior of steel fibre lightweight concrete wall panel under one way in plane action / Norfariza Ismail

Ismail, Norfariza (2014) Strength and behavior of steel fibre lightweight concrete wall panel under one way in plane action / Norfariza Ismail. Masters thesis, Universiti Teknologi MARA.

Abstract

Nowadays, with the rapid development of high rise building, larger size and span concrete structures are required. Wall panel is a structural element that considered as a vertical load bearing member that carries weight from the roof to the ground floor and to the foundation. A lower density from lightweight concrete decreases the weight of the building. However, lightweight concrete having a lower module of elasticity has a faster rate of crack development in reinforced concrete members. By adding steel fibre, it will reduce the macro-cracking. The strength and behavior of steel fibre lightweight concrete, the ultimate load and crack pattern are investigated. This research was using sample size with constant on the height and thickness that is 600 mm and 40 mm respectively to give the constant slenderness ratio (SR=15). The length was varies from 320 mm, 400 mm, 560 mm and 800 mm provide the range of aspect ratio (AR = 1.875, 1.5, 1.07 and 0.75). Use 0.5% steel fibre of 35 mm length with 0.55 mm diameter and 30% Expanded Polystyrene (EPS). From this research, it has been found that the maximum deflection occurs at the wall panel with AR 0.75 that is 8.28 mm with an average ultimate load of 127.78 kN. The maximum lateral displacement for four (4) wall panels occured at the 0.5 wall height (0.5H) of wall panel that is at 300 mm height. Maximum crack length for each wall panels SFLWC-1 crack length is 30 cm at front, SFLWC-2 crack length is 25 cm at rear, SFLWC-3 crack length is 30 cm at rear and SFLWC-4 crack length is 55 cm at front. The crack pattern from this study shows a concrete crushing at the top and bottom of the wall panels. This shows that the failure at top support was due to applied load and at bottom end was due to support condition. Besides that, the panel with the low aspect ratio tends to fail by crushing, while a panel with high aspect ratio tends to fail by buckling. It concluded the strength and behavior of steel fibre lightweight concrete wall panel under one way in plane action has been revealed by determination of ultimate load, deflection profile, crack patterns, crack loading, failure modes, deformation profile and stress strain relationship as discussed.

Metadata

Item Type: Thesis (Masters)
Creators:
Creators
Email / ID Num.
Ismail, Norfariza
2012679946
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Civil Engineering
Programme: Master of Structural Engineering
Keywords: Strength; Steel fibre; Lightweight concrete wall panel
Date: July 2014
URI: https://ir.uitm.edu.my/id/eprint/18426
Edit Item
Edit Item

Download

[thumbnail of TM_NORFARIZA ISMAIL EC 14_5.pdf] Text
TM_NORFARIZA ISMAIL EC 14_5.pdf

Download (95kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:

ID Number

18426

Indexing

Statistic

Statistic details