Studies on intermetallics and physical properties of Sn-3.5Ag-1.0Cu lead free solder with Zn additive / Iziana Yahya

Yahya, Iziana (2016) Studies on intermetallics and physical properties of Sn-3.5Ag-1.0Cu lead free solder with Zn additive / Iziana Yahya. Masters thesis, Universiti Teknologi MARA.

Abstract

The need for replacing lead based solder has received great attention among researchers because of their toxicity. The Sn-Ag-Cu family is the most promising candidate. However, these solder systems need better improvement in terms of controlling their intermetallic formation, growth rate and also their mechanical properties. In this study, the Sn-3.5Ag-l.0Cu solder was studied and three different amounts of Zn were added into the solder system. The solder was prepared using powder metallurgy method. It was characterized for their melting temperature, hardness and density. For intermetallic study, the solder was melted at 250°C on a Cu substrate and placed in an oven at 150°C until 1000 h. After the aging process, the solder joint was cross-sectioned and analysed under a Scanning Electron Microscope and Energy Dispersive X-ray. The thickness of Cu₆Sn₅ and Cu₃ Sn intermetallics were measured using image J software and their growths kinetic were calculated. The shear joint specimen was aged until 1000 h and the joint strength test was performed using an Instron machine. The addition of Zn has no significant effect on their melting temperature. Density and hardness results show that the optimum condition in preparation of solder disc was 2 h is mixing time and 14 MPa pressure. The addition of Zn retarded the growth of the intermetallic with 0.4 wt.% Zn gives the most significant values compared to 0.1 and 0.7 wt.% Zn addition. The growth of intermetallic compounds followed a parabolic law, implying that the growth of the intermetallic layer was diffusion control. The addition of 0.4 wt.% Zn gives the smallest growth constant (k) which are 0.16 x 10⁻¹⁴, 2.56 x 10⁻¹⁴ and 4.00 x 10⁻¹⁴ cm²/s for Cu₆Sn₅, Cu₃Sn and total intermetallic, respectively. Smaller k value indicates that the growth of intermetallic was slower and thus Zn retards the intermetallic growth. The decreasing of solder joint strength as aging time increases can be correlated to the growth of the intermetallic. Solder composition with the addition of 0.7 wt.% Zn has the highest stress values which is 20.14 MPa for as-soldered and 15.30 MPa for 1000 h aging time.

Metadata

Item Type: Thesis (Masters)
Creators:
Creators
Email / ID Num.
Yahya, Iziana
UNSPECIFIED
Contributors:
Contribution
Name
Email / ID Num.
Thesis advisor
Mayappan, Ramani
UNSPECIFIED
Subjects: T Technology > TA Engineering. Civil engineering > Materials of engineering and construction > Intermetallic compounds
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Programme: Master of Science - AS780
Keywords: Intermetallics; Physical properties; Solder; Zn additive
Date: 2016
URI: https://ir.uitm.edu.my/id/eprint/17882
Edit Item
Edit Item

Download

[thumbnail of 17882.pdf] Text
17882.pdf

Download (149kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:
On Shelf

ID Number

17882

Indexing

Statistic

Statistic details