A study of waste polyester fabric used as filler in natural rubber compound / Ruqaiyah Abdul Rahim

Abdul Rahim, Ruqaiyah (2009) A study of waste polyester fabric used as filler in natural rubber compound / Ruqaiyah Abdul Rahim. Degree thesis, Universiti Teknologi MARA.

Abstract

The effects of the waste polyester fabric used as filler in natural rubber compound were studied. Six types of testing were conducted to determine the properties of waste polyester fabric used as filler in natural rubber compound such as the tensile testing, hardness test, resilience test, ageing test, density test and Mooney viscosity. The phase morphology for tensile surface failure of rubber compound was observed. NR compounded with waste polyester fabrics by using internal mixer machine and two roll mills machine. The physical properties of these composite were investigated. The results show the physical properties of NR compound without filler for tensile is better than NR compound with filler. The hardness, resilience, density and Mooney viscosity of NR compound with filler is better than NR compound without filler. The tensile surface failure has been studied by using Field Emission Scanning Electron Microscopy (FESEM) shows that the waste polyester fabrics and NR compound were mixed together with poor bonding between each other.

Metadata

Item Type: Thesis (Degree)
Creators:
Creators
Email / ID Num.
Abdul Rahim, Ruqaiyah
UNSPECIFIED
Subjects: T Technology > TS Manufactures > Textile fabrics > Synthetic textile fibers > Polyesters
T Technology > TS Manufactures > Rubber industry
Divisions: Universiti Teknologi MARA, Shah Alam > Faculty of Applied Sciences
Keywords: Waste polyester fabric, filler, natural rubber compound
Date: 2009
URI: https://ir.uitm.edu.my/id/eprint/13709
Edit Item
Edit Item

Download

[thumbnail of TD_RUQAIYAH ABDUL RAHIM AS 09_5 1.pdf] Text
TD_RUQAIYAH ABDUL RAHIM AS 09_5 1.pdf

Download (537kB)

Digital Copy

Digital (fulltext) is available at:

Physical Copy

Physical status and holdings:
Item Status:

ID Number

13709

Indexing

Statistic

Statistic details